  • ASTM A1064/A1064M-15

ASTM A1064/A1064M-15

Standard Specification for Carbon-Steel Wire and Welded Wire Reinforcement, Plain and Deformed, for Concrete

ASTM International, 03/01/2015

Publisher: ASTM

File Format: PDF

$32.00$65.00


Published:01/03/2015

Pages:11

File Size:1 file , 170 KB

Note:This product is unavailable in Russia, Ukraine, Belarus

1.1 This specification covers carbon-steel wire and welded wire reinforcement produced from hot-rolled rod to be used for the reinforcement of concrete. The steel wire is cold-worked, drawn or rolled, plain (non-deformed, as-drawn or galvanized), or deformed. Welded wire reinforcement is made from plain or deformed wire, or a combination of plain and deformed wire. Common wire sizes and dimensions are given in Table 1, Table 2, Table 3, and Table 4. Actual wire sizes are not restricted to those shown in the tables.

(A) Table 1 should be used on projects that are designed using inch-pound units; Table 2 should be used on projects that are designed using SI units.
(B) The number following the prefix indicates the nominal cross-sectional area of the wire in square inches multiplied by 100.
(C) For sizes other than those shown above, the Size Number shall be the number of one hundredth of a square inch in the nominal area of the wire cross section, prefixed by the W.
(D) These sizes represent the most readily available sizes in the welded wire reinforcement industry. Other wire sizes are available and many manufactures can produce them in 0.0015 in.² increments.
(E) The nominal diameter is based on the nominal area of the wire.
(A) The wire sizes in Table 1 should be used on projects that are designed using inch-pound units; the wire sizes in Table 2 should be used on projects that are designed using SI units.
(B) The number following the prefix indicates the nominal cross-sectional area of the wire in square milimetres.
(C) For sizes other than those shown above, the Size Number shall be the number of square millimetres in the nominal area of the wire cross section, prefixed by the MW.
(D) These sizes represent the most readily available sizes in the welded wire reinforcement industry. Other wire sizes are available and many manufactures can produce them in 1 mm² increments.
(E) The nominal diameter is based on the nominal area of the wire.
(A) The wire sizes in Table 3 should be used on projects that are designed using inch-pound units; the wire sizes in Table 4 should be used on projects that are designed using SI units.
(B) The number following the prefix indicates the nominal cross-sectional area of the deformed wire in square inches multiplied by 100.
(C) For sizes other than those shown above, the Size Number shall be the number of one hundredths of a square inch in the nominal area of the deformed wire cross section, prefixed by the D.
(D) These sizes represent the most readily available sizes in the welded wire reinforcement industry. Other wire sizes are available and many manufacturers can produce them in 0.0015 in.² increments.
(E) The nominal diameter of a deformed wire is equivalent to the nominal diameter of a plain wire having the same weight per foot as the deformed wire.
(F) The cross-sectional area is based on the weight of the wire. The area in square inches may be calculated by dividing the weight in pounds by 0.2833 (weight of 1 in.³ of steel) or by dividing the weight per lineal foot of specimen in pounds by 3.4 (weight of steel 1 in. square and 1 foot long).
(G) The minimum average height of the deformations shall be determined from measurements made on not less than two typical deformations from each line of deformations on the wire. Measurements shall be made at the center of indentation or between two raised ribs as described in 7.2.4.7.
(H) Spacing of deformations shall not be greater than 0.285 in. nor less than 0.182 in. for all wire sizes.
(I) See 7.2.4.3 for average number of deformations per unit length.
(A) The wire sizes in Table 3 should be used on projects that are designed using inch-pound units; the wire sizes in Table 4 should be used on projects that are designed using SI units.
(B) The number following the prefix indicates the nominal cross-sectional area of the deformed wire in square millimetres.
(C) For sizes other tha

More ASTM standard pdf

ASTM D129-11

ASTM D129-11

Standard Test Method for Sulfur in Petroleum Products (General High Pressure Decomposition Device Method)

$30.00 $60.00

ASTM D2196-15

ASTM D2196-15

Standard Test Methods for Rheological Properties of Non-Newtonian Materials by Rotational Viscometer

$31.00 $62.00

ASTM E1171-01

ASTM E1171-01

Standard Test Method for Photovoltaic Modules in Cyclic Temperature and Humidity Environments

$25.00 $50.00

ASTM C1651-11

ASTM C1651-11

Standard Test Method for Measurement of Roll Wave Optical Distortion in Heat-Treated Flat Glass

$30.00 $60.00