• ASTM A335/A335M-18

ASTM A335/A335M-18

Standard Specification for Seamless Ferritic Alloy-Steel Pipe for High-Temperature Service

ASTM International, 03/01/2018

Publisher: ASTM

File Format: PDF

$29.00$58.00


Published:01/03/2018

Pages:10

File Size:1 file , 130 KB

Note:This product is unavailable in Russia, Ukraine, Belarus

1.1 This specification2 covers nominal wall and minimum wall seamless ferritic alloy-steel pipe intended for high-temperature service. Pipe ordered to this specification shall be suitable for bending, flanging (vanstoning), and similar forming operations, and for fusion welding. Selection will depend upon design, service conditions, mechanical properties, and high-temperature characteristics.

1.2 Several grades of ferritic steels (see Note 1) are covered. Their compositions are given in Table 1.

Note 1: Ferritic steels in this specification are defined as low- and intermediate-alloy steels containing up to and including 10 % chromium.

(A) New designation established in accordance with Practice E527 and SAE J1086, Practice for Numbering Metals and Alloys (UNS).
(B) Grade P5c shall have a titanium content of not less than 4 times the carbon content and not more than 0.70 %; or a columbium content of 8 to 10 times the carbon content.
(C) Alternatively, in lieu of this ratio minimum, the material shall have a minimum hardness of 275 HV in the hardened condition, defined as after austenitizing and cooling to room temperature but prior to tempering. Hardness testing shall be performed at mid-thickness of the product. Hardness test frequency shall be two samples of product per heat treatment lot and the hardness testing results shall be reported on the material test report.
(D) Applies to both heat and product analyses.

1.3 Supplementary requirements (S1 to S8) of an optional nature are provided. Supplementary requirements S1 through S6 call for additional tests to be made, and when desired, shall be so stated in the order together with the number of such tests required.

1.4 The values stated in either SI units or inch-pound units are to be regarded separately as standard. Within the text, the SI units are shown in brackets. The values stated in each system may not be exact equivalents; therefore, each system shall be used independently of the other. Combining values from the two systems may result in non-conformance with the standard. The inch-pound units shall apply unless the “M” designation of this specification is specified in the order.

Note 2: The dimensionless designator NPS (nominal pipe size) has been substituted in this standard for such traditional terms as “nominal diameter,” “size,” and “nominal size.”

1.5 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

More ASTM standard pdf

ASTM C457/C457M-10a

ASTM C457/C457M-10a

Standard Test Method for Microscopical Determination of Parameters of the Air-Void System in Hardened Concrete

$33.00 $67.00

ASTM D7724-11(2016)

ASTM D7724-11(2016)

Standard Test Method for Carbon Black-Non-Dispersible Matter by Mechanical Flushing (NDM)

$25.00 $50.00

ASTM C1207-10

ASTM C1207-10

Standard Test Method for Nondestructive Assay of Plutonium in Scrap and Waste by Passive Neutron Coincidence Counting

$33.00 $67.00

ASTM C1140-03

ASTM C1140-03

Standard Practice for Preparing and Testing Specimens from Shotcrete Test Panels

$26.00 $52.00