1.1 This specification2 covers heat-treated carbon-manganese-silicon steel plates intended for fusion welded pressure vessels and structures.
1.2 Plates furnished under this specification are available in the following three classes:
Class
Heat Treatment
Thickness
Yield Strength, min, ksi [MPa]
Tensile Strength, min, ksi [MPa]
1
Normalized
21/2 in. and under [65 mm and under]
50 [345]
70 [485]
Over 21/2 to 4 in. [Over 65 to 100 mm]
45 [310]
65 [450]
2
Quenched and tempered
60 [415]
80 [550]
55 [380]
75 [515]
Over 4 to 6 in. [Over 100 to 150 mm]
46 [315]
3
40 [275]
1.3 The maximum thickness of plates furnished under this specification is 4 in. [100 mm] for Class 1 and 6 in. [150 mm] for Class 2 and Class 3.
1.4 The values stated in either inch-pound units or SI units are to be regarded separately as standard. Within the text, the SI units are shown in brackets. The values stated in each system are not exact equivalents; therefore, each system is to be used independently of the other without combining values in any way.
1.5 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.
Standard Test Method for Average Velocity in a Duct (Pitot Tube Method)
$38.00 $76.00
Standard Specification for Steel Sheet, 55 % Aluminum-Zinc Alloy-Coated by the Hot-Dip Process
$30.00 $60.00
Standard Test Method for Interfacial Tension of Oil Against Water by the Ring Method
$21.00 $43.20
Standard Terminology Relating to Petroleum, Petroleum Products, and Lubricants
$44.00 $89.00