• ASTM A831/A831M-95(2000)

ASTM A831/A831M-95(2000)

Standard Specification for Austenitic and Martensitic Stainless Steel Bars, Billets, and Forgings for Liquid Metal Cooled Reactor Core Components (Withdrawn 2005)

ASTM International, 01/01/2000

Publisher: ASTM

File Format: PDF

$29.00$58.00


Published:01/01/2000

Pages:5

File Size:1 file , 42 KB

Note:This product is unavailable in Russia, Ukraine, Belarus

1.1 This specification covers hot- and cold-finished austenitic and martensitic stainless steel bars, billets, and forgings intended for use in manufacturing core components used at high temperatures in liquid metal cooled nuclear reactors.

1.2 The bars, billets, and forgings are intended for machining, welding, hot- and cold-forming operations.

1.3 The values stated in either inch-pound units or SI units are to be regarded separately as standard. Within the text, the SI units are shown in brackets. The values stated in each system are not exact equivalents; therefore, each system shall be used independently of the other. Combining values from the two systems may result in nonconformance with the specification.

1.4 This specification and the applicable material specifications are expressed in both inch-pound and SI units. However, unless the order specifies the applicable "M" specification designation (SI units), the material shall be furnished in inch-pound units.

More ASTM standard pdf

ASTM C1543-10a

ASTM C1543-10a

Standard Test Method for Determining the Penetration of Chloride Ion into Concrete by Ponding (Withdrawn 2019)

$26.00 $52.00

ASTM C1364-10a

ASTM C1364-10a

Standard Specification for Architectural Cast Stone

$26.00 $52.00

ASTM D4601-98

ASTM D4601-98

Standard Specification for Asphalt-Coated Glass Fiber Base Sheet Used in Roofing

$25.00 $50.00

ASTM D7639-10(2014)

ASTM D7639-10(2014)

Standard Test Method for Determination of Zirconium Treatment Weight or Thickness on Metal Substrates by X-Ray Fluorescence

$26.00 $52.00