Standard Specification for Electric Fusion Welded Nickel and Nickel Alloy Pipe

ASTM International, 10/01/2009

Publisher: ASTM

File Format: PDF

$30.00$60.00


Published:01/10/2009

Pages:8

File Size:1 file , 150 KB

Note:This product is unavailable in Russia, Ukraine, Belarus

1.1 This specification covers electric fusion welded pipe suitable for high-temperature or corrosive service as listed in Table 1. (Although no restrictions are placed on the sizes of pipe that may be furnished under this specification, commercial practice is commonly limited to sizes not less than 8 in. (203 mm) nominal diameter.)

1.2 Five classes of pipe are covered as follows:

1.2.1 Class 1 - Pipe shall be double welded by processes employing filler metal in all passes and shall be completely radiographed.

1.2.2 Class 2 - Pipe shall be double welded by processes employing filler metal in all passes. No radiography is required.

1.2.3 Class 3 - Pipe shall be single welded by processes employing filler metal in all passes and shall be completely radiographed.

1.2.4 Class 4 - Same as Class 3 except that the weld pass exposed to the inside pipe surface may be made without the addition of filler metal.

1.2.5 Class 5 - Pipe shall be double welded by processes employing filler metal in all passes and shall be spot radiographed.

1.3 The values stated in inch-pound units are to be regarded as standard. The values given in parentheses are mathematical conversions to SI units that are provided for information only and are not considered standard.

1.4 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to become familiar with all hazards including those identified in the appropriate Material Safety Data Sheet (MSDS) for this product/material as provided by the manufacturer, to establish appropriate safety and health practices, and determine the applicability of regulatory limitations prior to use.

TABLE 1 Recommended Heat Treatment

Alloy UNS Designation PWHTA, B
Deg. F. (Deg. C)
Quench
200 (Ni) N02200 1650-1700 (900 to 928) Rapid Air/water
201 (Low C) N02201 1650-1700 (900 to 928) Rapid Air/water
400 (Ni-Cu) N04400 1650-1700 (900 to 928) Rapid Air/water
X (Ni-Cr-Mo-Fe) N06002 2150 (1177)C Rapid Air/water
C22D (Low C-Ni-Mo-Cr) N06022 2050-(1120)C Rapid Air/water
G30D (Ni-Cr-Fe-Mo-Cu) N06030 2150 (1177)C Rapid Air/water
C2000D(Ni-Cr-Mo-Cu) N06200 2075-2125 (1135-1163)B Rapid Air/water
230D (Ni-Cr-W-Mo) N06230 2150-2250 (1177-1232)B Rapid Air/water
600 (Ni-Cr-Fe) N06600 1800-1850 (983 to 1010) Rapid Air/water
601 (Ni-Cr-Fe-Al) N06601 1600-1650 (874 to 900)E Rapid Air/water
625 (Ni-Cr-Mo-Cb) Grade 1 N06625 1600 (871)C Rapid Air/water
625 (Ni-Cr-Mo-Cb) Grade 2 N06625 2000 (1093)C Rapid Air/water
G3D (Ni-Cr-Fe-Mo-Cu) N06985 2100-2150 (1147 to 1177)B Rapid Air/water
Alloy 20 (Cr-Ni-Fe-Mo-Cu-Cb) N08020 1700-1850 (927 to 1010) Rapid Air/water
... N08024 1925-1975 (1052 to 1079) Rapid Air/water
... N08026 2050-2200 (1121 to 1204) Rapid Air/water
825 (Ni-Fe-Cr-Mo-Cu) N08825 1700-1800 (930 to 980)E Rapid Air/water
C276 (Low C-Ni-Mo-Cr) N10276 2050 (1121)C Rapid Air/water
B2 (Ni-Mo) N10665 1950 (1065)C Rapid Air/water
B3D (Ni-Mo) N10675 1950 (1065)C

More ASTM standard pdf

ASTM C1322-05b(2010)

ASTM C1322-05b(2010)

Standard Practice for Fractography and Characterization of Fracture Origins in Advanced Ceramics

$47.00 $94.00

ASTM F152-95(2002)

ASTM F152-95(2002)

Standard Test Methods for Tension Testing of Nonmetallic Gasket Materials

$26.00 $52.00

ASTM E1672-95

ASTM E1672-95

Standard Guide for Computed Tomography (CT) System Selection

$29.00 $58.00

ASTM C1519-10

ASTM C1519-10

Standard Test Method for Evaluating Durability of Building Construction Sealants by Laboratory Accelerated Weathering Procedures

$30.00 $60.00