Standard Specification for Thin Veneer Brick Units Made From Clay or Shale

ASTM International, 03/01/2023

Publisher: ASTM

File Format: PDF

$28.00$57.00


Published:01/03/2023

Pages:5

File Size:1 file , 450 KB

Note:This product is unavailable in Russia, Ukraine, Belarus

1.1 This specification covers thin veneer brick units made from clay, shale, fire clay, sand, or mixtures thereof, and fired to incipient fusion for use in adhered or fastened veneer applications. Three types of thin veneer brick units in each of two grades are covered. In this specification, the term thin veneer brick shall be understood to mean a clay masonry unit with a thickness of less than 25/8 in. (66.7 mm).
Note 1: Thin brick with thicknesses greater than 1³/4 in. (44.5 mm) may exceed the prescriptive unit weight limits for adhered masonry veneer. In such cases, rational design is necessary. Alternatively, use of a system or construction method designed to accommodate thin brick units exceeding 1³/4 in. (44.5 mm) in thickness may be an option.
1.2 The property requirements of this specification apply at the time of purchase. The use of results from testing of brick extracted from masonry structures for determining conformance or nonconformance to the property requirements (Section 7) of this specification is beyond the scope of this specification.
1.3 The brick are prismatic units available in a variety of sizes, textures, colors, and shapes. This specification is not intended to provide specifications for paving brick (see Specification C902).
1.4 Brick covered by this specification are manufactured from clay, shale, or similar naturally occurring substances and subjected to a heat treatment at elevated temperatures (firing). The heat treatment must develop sufficient fired bond between the particulate constituents to provide the strength and durability requirements of the specification. (See "firing" and "fired bond" in Terminology C1232.)
1.5 Thin brick are shaped during manufacture by molding, pressing, or extrusion. The shaping method is a way to describe the thin brick. Thin brick may also be cut from thicker masonry units.
1.5.1 This standard and its individual requirements shall not be used to qualify or corroborate the performance of a masonry unit made from other materials, or made with other forming methods, or other means of binding the materials.
1.6 The text of this specification references notes and footnotes which provide explanatory material. These notes and footnotes (excluding those in tables and figures) shall not be considered as requirements of the standard.
1.7 The values stated in inch-pound units are to be regarded as standard. The values given in parentheses are mathematical conversions to SI units that are provided for information only and are not considered standard.
1.8 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

More ASTM standard pdf

ASTM F948-94(2001)

ASTM F948-94(2001)

Standard Test Method for Time-to-Failure of Plastic Piping Systems and Components Under Constant Internal Pressure With Flow

$29.00 $58.00

ASTM D7471-09

ASTM D7471-09

Standard Specification for CPT-Fluoropolymer Molding and Extrusion Materials

$25.00 $50.00

ASTM D2047-99

ASTM D2047-99

Standard Test Method for Static Coefficient of Friction of Polish-Coated Floor Surfaces as Measured by the James Machine

$25.00 $50.00

ASTM D6498-99

ASTM D6498-99

Standard Guide for Household Hazardous Waste Training Outline for Household Hazardous Waste Collection Operations

$29.00 $58.00