• ASTM C31/C31M-22

ASTM C31/C31M-22

Standard Practice for Making and Curing Concrete Test Specimens in the Field

ASTM International, 08/01/2022

Publisher: ASTM

File Format: PDF

$34.00$68.00


Published:01/08/2022

Pages:7

File Size:1 file , 120 KB

Note:This product is unavailable in Russia, Ukraine, Belarus

1.1 This practice covers procedures for making and curing cylinder and beam specimens from representative samples of fresh concrete for a construction project.
1.2 The concrete used to make the molded specimens shall be sampled after all on-site adjustments have been made to the mixture proportions, including the addition of mix water and admixtures. This practice is not intended for making specimens from concrete not having measurable slump or requiring other sizes or shapes of specimens.
1.3 This practice is not applicable to lightweight insulating concrete or controlled low strength material (CLSM).
Note 1: Test Method C495/C495M covers the preparation of specimens and the determination of the compressive strength of lightweight insulating concrete. Test Method D4832 covers procedures for the preparation, curing, transporting and testing of cylindrical test specimens of CLSM.
1.4 The values stated in either SI units or inch-pound units are to be regarded separately as standard. The values stated in each system may not be exact equivalents; therefore, each system shall be used independently of the other. Combining values from the two systems may result in non-conformance with the standard.
1.5 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use. (Warning-Fresh hydraulic cementitious mixtures are caustic and may cause chemical burns to exposed skin and tissue upon prolonged exposure.2)
1.6 The text of this standard references notes which provide explanatory material. These notes shall not be considered as requirements of the standard.
1.7 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

More ASTM standard pdf

ASTM D5961/D5961M-01

ASTM D5961/D5961M-01

Standard Test Method for Bearing Response of Polymer Matrix Composite Laminates

$43.00 $86.00

ASTM D36/D36M-12

ASTM D36/D36M-12

Standard Test Method for Softening Point of Bitumen (Ring-and-Ball Apparatus)

$26.00 $52.00

ASTM A852/A852M-01

ASTM A852/A852M-01

Standard Specification for Quenched and Tempered Low-Alloy Structural Steel Plate with 70 ksi [485 MPa] Minimum Yield Strength to 4 in. [100 mm] Thick

$26.00 $52.00

ASTM B550/B550M-07(2012)

ASTM B550/B550M-07(2012)

Standard Specification for Zirconium and Zirconium Alloy Bar and Wire

$30.00 $60.00