• ASTM D7766/D7766M-23

ASTM D7766/D7766M-23

Standard Practice for Damage Resistance Testing of Sandwich Constructions

ASTM International, 05/01/2023

Publisher: ASTM

File Format: PDF

$28.00$57.00


Published:01/05/2023

Pages:10

File Size:1 file , 430 KB

Note:This product is unavailable in Russia, Ukraine, Belarus

1.1 This practice provides instructions for modifying laminate quasi-static indentation and drop-weight impact test methods to determine damage resistance properties of sandwich constructions. Permissible core material forms include those with continuous bonding surfaces (such as balsa wood and foams) as well as those with discontinuous bonding surfaces (such as honeycomb, truss cores and fiber-reinforced cores).
1.2 This practice supplements Test Methods D6264/D6264M (for quasi-static indentation testing) and D7136/D7136M (for drop-weight impact testing) with provisions for testing sandwich specimens. Several important test specimen parameters (for example, facing thickness, core thickness and core density) are not mandated by this practice; however, repeatable results require that these parameters be specified and reported.
1.3 Three test procedures are provided. Procedures A and B correspond to D6264/D6264M test procedures for rigidlybacked and edge-supported test conditions, respectively. Procedure C corresponds to D7136/D7136M test procedures. All three procedures are suitable for imparting damage to a sandwich specimen in preparation for subsequent damage tolerance testing in accordance with Test Method D8287/D8287M (compressive loading) and Practice D8388/D8388M (flexural loading).
1.4 In general, Procedure A is considered to be the most suitable procedure for comparative damage resistance assessments, due to reduced influence of flexural stiffness and support fixture characteristics upon damage formation. However, the selection of a test procedure and associated support conditions should be done in consideration of the intended structural application, and as such Procedures B and C may be more appropriate for comparative purposes for some applications.
1.5 Units-The values stated in either SI units or inch-pound units are to be regarded separately as standard. The values stated in each system are not necessarily exact equivalents; therefore, to ensure conformance with the standard, each system shall be used independently of the other, and values from the two systems shall not be combined.
1.5.1 Within the text the inch-pound units are shown in brackets.
1.6 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use.
1.7 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

More ASTM standard pdf

ASTM B328-96

ASTM B328-96

Standard Test Method for Density, Oil Content, and Interconnected Porosity of Sintered Metal Structural Parts and Oil-Impregnated Bearings

$25.00 $50.00

ASTM D7003/D7003M-03(2013)e1

ASTM D7003/D7003M-03(2013)e1

Standard Test Method for Strip Tensile Properties of Reinforced Geomembranes

$27.00 $54.00

ASTM D1337-96

ASTM D1337-96

Standard Test Method for Storage Life of Adhesives by Consistency and Bond Strength

$25.00 $50.00

ASTM D6152-99(2005)

ASTM D6152-99(2005)

Standard Specification for SEBS-Modified Mopping Asphalt Used in Roofing

$26.00 $52.00