• ASTM D885/D885M-10a(2014)

ASTM D885/D885M-10a(2014)

Standard Test Methods for Tire Cords, Tire Cord Fabrics, and Industrial Filament Yarns Made from Manufactured Organic-Base Fibers

ASTM International, 05/15/2014

Publisher: ASTM

File Format: PDF

$43.00$86.00


Published:15/05/2014

Pages:31

File Size:1 file , 360 KB

Note:This product is unavailable in Russia, Ukraine, Belarus

1.1 These test methods cover the testing of industrial filament yarns made wholly of manufactured organic-base fibers, cords twisted from such yarns, fabrics woven from such cords, and products that are made specifically for use in the manufacture of pneumatic tires. They may be applied to similar yarns and cords used for reinforcing other rubber goods and for other industrial applications. The test methods apply to nylon, polyester, and rayon yarns and tire cords twisted from such yarns and to fabrics made from such cords. The yarn or cord may be wound on cones, tubes, bobbins, spools, or beams; may be woven into fabric; or may be in some other form. The methods include testing procedure only and include no specifications or tolerances.

1.2 No procedure is included for the determination of fatigue resistance of cord, but several commonly used procedures for the measurement of fatigue resistance of cords in rubber were published in the appendix of these test methods in the 1967 Annual Book of ASTM Standards, Part 24, and in earlier issues of Test Methods D885.

1.3 The sections on “Growth of Conditioned Yarns and Cords,” “Properties of Yarns and Cords at Elevated Temperature,” and “Properties of Wet Yarns and Cords” have been moved to Appendix X1 - Appendix X3 as non-mandatory informational items because of their very limited use by the industry and because precision and bias statements are not included.

1.4 This standard includes the following sections:

More ASTM standard pdf

ASTM D2386-06

ASTM D2386-06

Standard Test Method for Freezing Point of Aviation Fuels

$26.00 $52.00

ASTM D2143-00(2005)e1

ASTM D2143-00(2005)e1

Standard Test Method for Cyclic Pressure Strength of Reinforced, Thermosetting Plastic Pipe

$26.00 $52.00

ASTM C1468-06

ASTM C1468-06

Standard Test Method for Transthickness Tensile Strength of Continuous Fiber-Reinforced Advanced Ceramics at Ambient Temperature

$33.00 $67.00

ASTM D3882-99(2006)

ASTM D3882-99(2006)

Standard Test Method for Bow and Skew in Woven and Knitted Fabrics

$30.00 $60.00

 

Section

Adhesion of Cord to Elastomers

34

Bibliography of Tire Cord Test Methods

X5

Breaking Strength (Force) of Yarns and Cords at Elevated Tempera-
 ture

X2.3

Breaking Strength (Force) of Conditioned Yarns and Cords

16

Breaking Strength (Force) of Oven-Dried Rayon Yarns and Cords

23

Breaking Strength (Force) of Rayon Yarns and Cords at Specified
 Moisture Regain Level, Adjustment of

17

Breaking Tenacity of Conditioned Yarns and Cords

18

Breaking Tenacity of Oven-Dried Rayon Yarns and Cords

24

Breaking Toughness of Yarns and Cords

28

Commercial Mass

9

Conditioning

7

Contraction of Wet Yarns and Cords

X3

Count of Tire Cord Fabric

37

Dip (Adhesive) Solids Pickup on Yarns and Cords

33

Elongation at Break of Conditioned Yarns and Cords

19

Elongation at Break of Oven-Dried Rayon Yarns and Cords

25

Elongation of Rayon Yarns and Cords at a Specified Moisture Regain
 Level, Adjustment of Observed

20

Extractable Matter in Yarns and Cords

32

Force at Specified Elongation (FASE) of Conditioned Yarns and
 Cords

21

Force at Specified Elongation (FASE) of Oven-Dried Rayon Yarns and
 Cords

26

Growth of Conditioned Yarns and Cords

X1

Identification of Fibers

8

Keywords

40

Linear Density

11

Mass of per Unit Area of Tire Cord Fabric

36

Modulus of Conditioned Yarns and Cords

22

Moisture Regain, Actual

10

Precision and Bias of Certain Yarn and Cord Tests

39

 

35 to

Properties of Tire Cord Fabric

38

Sampling

6

Shrinkage Force of Conditioned Yarns and Cords at Elevated Temper-
 ature


X2.5

Shrinkage of Conditioned Yarns and Cords at Elevated Temperature

X2.4

Significance and Use, General

5

Significance and Use, Tensile Properties

14

SI Calculations (examples for work-to-break, specific work-to-break,
 and breaking toughness)


X4

Stiffness of Fabric

38

 

12 to