ASTM E399-08

Standard Test Method for Linear-Elastic Plane-Strain Fracture Toughness K Ic of Metallic Materials

ASTM International, 11/15/2008

Publisher: ASTM

File Format: PDF

$43.00$86.00

Description

Published:15/11/2008

Pages:33

File Size:1 file , 690 KB

Note:This product is unavailable in Russia, Ukraine, Belarus

1.1 This test method covers the determination of fracture toughness (K_Ic) of metallic materials under predominantly linear-elastic, plane-strain conditions using fatigue precracked specimens having a thickness of 1.6 mm (0.063 in.) or greater subjected to slowly, or in special (elective) cases rapidly, increasing crack-displacement force. Details of test apparatus, specimen configuration, and experimental procedure are given in the Annexes.

Note 1 - Plane-strain fracture toughness tests of thinner materials that are sufficiently brittle (see 7.1) can be made using other types of specimens (1). There is no standard test method for such thin materials.

1.2 This test method is divided into two parts. The first part gives general recommendations and requirements for K_Ic testing. The second part consists of Annexes that give specific information on displacement gage and loading fixture design, special requirements for individual specimen configurations, and detailed procedures for fatigue precracking. Additional annexes are provided that give specific procedures for beryllium and rapid-force testing.

1.3 General information and requirements common to all specimen configurations:

	Section
Referenced Documents	2
Terminology	3
Stress-Intensity Factor	3.1.1
Plane-Strain Fracture Toughness	3.1.2
Crack Plane Orientation	3.1.3
Summary of Test Method	4
Significance and Use	5
Significance	5.1
Precautions	5.1.1-5.1.5
Practical Applications	5.2
Apparatus (see also 1.4)	6
Tension Machine	6.1
Fatigue Machine	6.2
Loading Fixtures	6.3
Displacement Gage, Measurement	6.4
Specimen Size, Configurations, and Preparation (see also 1.5)	7
Specimen Size Estimates	7.1
Standard and Alternative Specimen Configurations	7.2
Fatigue Crack Starter Notches	7.3.1
Fatigue Precracking (see also 1.6)	7.3.2
Crack Extension Beyond Starter Notch	7.3.2.2
General Procedure	8
Specimen Measurements
Thickness	8.2.1
Width	8.2.2
Crack Size	8.2.3
Crack Plane Angle	8.2.4
Specimen Testing
Loading Rate	8.3
Test Record	8.4
Calculation and Interpretation of Results	9
Test Record Analysis	9.1
P_m_a_x/P_Q Validity Requirement	9.1.3
Specimen Size Validity Requirements	9.1.4
Reporting	11
Precision and Bias	12

1.4 Specific requirements related to test apparatus:

Double-Cantilever Displacement Gage	Annex A1
Testing Fixtures	Annex A2
Bend Specimen Loading Fixture	Annex A2.1
Compact Specimen Loading Clevis	Annex A2.2

1.5 Specific requirements related to individual specimen configurations:

Bend Specimen SE(B)	Annex A3
Compact Specimen C(T)	Annex A4
Disk-Shaped Compact Specimen DC(T)	Annex A5
Arc-Shaped Tension Specimen A(T)	Annex A6
Arc-Shaped Bend Specimen A(B)	Annex A7

1.6 Specific requirements related to special test procedures:

Fatigue Precracking KIc Specimens

Annex A8

Hot-Pressed Beryllium Testing

ASTM E399-08

Standard Test Method for Linear-Elastic Plane-Strain Fracture Toughness K Ic of Metallic Materials

More ASTM standard pdf

ASTM B702-93(1998)

ASTM D7198-05(2018)

ASTM E1258-88(1998)

ASTM E2015-99